ABSTRACT
Abstract
A separator for use in a lithium ion battery to provide a physical and electrically insulative mechanical barrier between confronting inner face surfaces of a negative electrode and a positive electrode may be formed predominantly of heat-resistant particles. The heat-resistant particles, which have diameters that range from about 0.01 μm to about 10 μm, are held together as a thin-layered, handleable, and unified mass by a porous inert polymer material. The high content of heat-resistant particles amassed between the confronting inner face surfaces of the negative and positive electrodes provides the separator with robust thermal stability at elevated temperatures. Methods for making these types of separators by a phase-separation process are also disclosed.
Description
TECHNICAL FIELD
The technical field of this disclosure relates generally to separators for a secondary lithium ion battery and, more specifically, to a separator formed predominantly of heat-resistant particles. The many heat-resistant particles are held together as a thin-layered, handleable, and unified mass by a porous inert polymer material. In an electrochemical battery cell of a lithium ion battery, the separator is situated between confronting inner face surfaces of a positive electrode and a negative electrode under an applied compressive force. Methods for making this type of separator by phase-separation are also disclosed.
BACKGROUND
Secondary (i.e., rechargeable) lithium ion batteries have been implemented as a power source into a wide variety of stationary and portable applications. Their structure and electrochemical reaction mechanism provide them with several desirable characteristics including a relatively high energy density, a relatively low internal resistance, a general non-appearance of any memory effect when compared to other types of rechargeable batteries, for example, nickel-cadmium batteries, and a low self-discharge rate. These characteristics have made lithium ion batteries the preferred mobile power source for portable consumer electronics such as laptop computers and cell phones. Larger-scale versions that interact with a multitude of interconnected systems have also been designed and manufactured by the automotive industry in an effort to improve vehicle fuel efficiency and reduce atmospheric pollution. The powertrains of hybrid electric vehicles (HEV) and extended range electric vehicles (EREV), for example, rely on the cooperative effort of lithium ion batteries and a hydrocarbon-fueled internal combustion engine to generate torque for vehicle propulsion.
A lithium ion battery generally contains one or more individual electrochemical battery cells that include a negative electrode, a positive electrode, and a porous polymeric separator sandwiched between the confronting inner face surfaces of the electrodes under a compressive force. The negative electrode generally includes a lithium host material that stores intercalated lithium at a relatively low electrochemical potential (relative to a lithium metal reference electrode). The positive electrode generally includes a lithium-based active material that stores intercalated lithium at a higher electrochemical potential than the lithium host material (relative to the same lithium metal reference electrode). The interadjacent porous separator includes opposed major surfaces that intimately contact the confronting inner face surfaces of the electrodes, and has typically been composed of a polyolefin such as polyethylene and/or polypropylene. A main function of the separator is to provide a porous and electrically insulative mechanical support barrier between the negative and positive electrodes. Each of the negative electrode, the positive electrode, and the separator is wetted with a liquid electrolyte solution that can communicate lithium ions. The liquid electrolyte solution is typically a lithium salt dissolved in a non-aqueous liquid solvent.
An interruptible external circuit electrically connects the negative electrode and the positive electrode to provide an electrical current path around the separator to electrochemically balance the migration of lithium ions. Metallic current collectors intimately associated with each electrode supply and distribute electrons to and from the external circuit depending on the operating state of the electrochemical battery cell. The external circuit can be coupled to an electrical load (during discharge) or an applied voltage from an external power source (during charging) through conventional electronic connectors and related circuitry. A voltage of approximately 2.5V to 4.3V is usually attained in each electrochemical battery cell during battery discharge. Greater overall battery power levels can be achieved, if necessary, by linking together a suitable number of similar electrochemical battery cells with their negative and positive electrodes connected in series or in parallel to corresponding common terminals. Current lithium ion batteries intended to be used in a vehicle powertrain typically include anywhere from 10 to 150 individual electrochemical battery cells. Several of these lithium ion batteries can be further connected in series or in parallel and packaged together to form a lithium ion battery pack that achieves a desired overall voltage and current capacity.
The individual electrochemical battery cell of a lithium ion battery operates by reversibly transporting lithium ions between the negative electrode and the positive electrode. The liquid electrolyte solution facilitates transport of the lithium ions through the separator. The flow direction of the lithium ions depends on whether the electrochemical batter cell is operating in a discharge state or a charge state. The lithium ions migrate from the negative electrode to the positive electrode during discharge and vice-versa during charging. The flow direction of the electrons through the external circuit mimics that of the lithium ions.
The discharge phase of the electrochemical battery cell can proceed when the negative electrode contains a sufficiently high concentration of intercalated lithium while the positive electrode is sufficiently depleted. The interruptible external circuit, when closed, provokes extraction of the intercalated lithium from the negative electrode. The extracted lithium splits into lithium ions and electrons. The lithium ions dissolve into the liquid electrolyte solution and migrate through the separator towards the positive electrode where they intercalate into the lithium-based active material. The electrons flow through the external circuit from the negative electrode to the positive electrode (with the help of the metallic current collectors) to balance these half-reactions. The flow of electrons through the external circuit can be harnessed and fed through the external load until the concentration of intercalated lithium in the negative electrode falls below a minimum effective level or the external circuit is opened.
The charge phase of the electrochemical battery cell can proceed after a partial or full reduction of its available capacity (through the discharge phase). To charge or re-power the cell, the external circuit is subjected to an applied voltage that originates from an external power source and which is sufficient in magnitude to accomplish charging in a reasonable time frame. The applied voltage drives the reverse of the discharge phase electrochemical half reactions; that is, during charging, intercalated lithium is extracted from the positive electrode to produce lithium ions and electrons. The lithium ions are carried back to the negative electrode through the separator and the electrons are driven back to the negative electrode through the external circuit. The lithium ions and the electrons reunite and replenish the negative electrode with intercalated lithium for the next battery discharge phase. Many thousands of substantially full-power discharge/charge cycles can be accomplished over the practical lifetime of the electrochemical battery cell.
The lifetime and performance of the electrochemical battery cell can be adversely impacted by a wide variety of expected and unforeseen factors. Exposure of the electrochemical battery cell to temperatures of 100° C. and above can cause the polyolefin separator to shrink, soften, and even melt if the temperature approaches 130° C. Such high temperatures can be attributed to charging-phase heat generation, ambient atmospheric temperature, or some other source. The temperature-initiated physical distortion of the polyolefin separator may ultimately permit direct electrical contact between the negative and positive electrodes and cause the electrochemical cell to short-circuit. Battery thermal runaway is also a possibility if the electrodes come into direct electrical contact with one another to an appreciable extent. A separator that can function reliably at the high-temperatures possibly encountered in an electrochemical battery cell of a lithium ion battery without affecting lithium ion movement is therefore needed.
SUMMARY OF THE DISCLOSURE
A separator for use in a lithium ion battery that retains its functionality at high operating temperatures includes a collection of heat-resistant particles held together in a thin, handleable layer by a relatively small amount of a porous inert polymer material. The heat-resistant particles range in size from about 0.01 μm to about 10 μm and are randomly stacked and arranged to a thickness of about 20 μm to about 50 μm with the outermost, surface exposed heat-resistant particles delineating opposed major face surfaces of the separator. The many heat-resistant particles naturally form a coextensive network of interconnected interstices that extends through the separator between the opposed major face surfaces. The porous inert polymer material pervades these naturally-formed interstices to bond and hold the heat-resistant particles together as a unified, handleable mass yet still permit infiltration of an appropriate liquid electrolyte solution.
The heat-resistant particles are thermally stable at temperatures below 250° C. They may be ceramic particles, cross-linked thermoset polymer particles, and/or engineering thermoplastic polymer particles. Some examples of suitable ceramic particles include alumina, titania, silica, ceria, zirconia, silicon carbide, boron carbide, titanium nitride, silicon nitride, titanium silicide, tungsten silicide, aluminum boride, titanium boride, mullite, spodumene, zirconium silicate, sillimanite, and petalite. Some examples of suitable cross-linked thermoset polymer particles include those of polyimides, polyurethanes, phenol-formaldehyde resins, melamine formaldehyde resins, and epoxy resins. Some examples of suitable engineering thermoplastic polymer particles include those of a polyimide, polyethylene terephthalate, polyphenylene sulfide, polyetherketone, polyether ether ketone, polyphenylsulfone, and a polysulfone. The porous inert polymer material that holds together the heat-resistant particles may be any polymer material suitable for use in the operating environment of a lithium ion battery. Some examples of the porous inert polymer material include polyetherimide (PEI), polyvinylidene fluoride (PVdF), polyacrylonitrile (PAN), poly(methyl methacrylate) (PMMA), polyoxymethylene (POM), or mixtures thereof. The porosity or void volume of the porous inert polymer material is preferably about 20% to about 80%.
The separator is intended to be used in the assembly of an electrochemical battery cell for a lithium ion battery. The separator may be situated between a negative electrode and a positive electrode and be infiltrated with an appropriate liquid electrolyte solution. The heat-resistant particles present on the major face surfaces of the separator contact confronting inner face surfaces of the negative and positive electrodes under an applied compressive force. The separator electrically insulates and physically separates the electrodes to prevent a short-circuit while remaining permeable to the internal passage of lithium ions (and related anions) through the liquid electrolyte solution. When assembled, the entire thickness of the electrochemical cell (positive electrode, negative electrode, and separator) is usually between about 80 μm and about 350 μm. A plurality of these electrochemical cells, often numbering from 10 to 150, can be connected in series or in parallel with many other electrochemical cells to form a lithium ion battery which, in turn, can be connected in series or in parallel with several other lithium ion batteries to form a lithium ion battery pack. The relatively thin and flexible nature of the electrochemical cells allows them to be rolled, folded, bent, or otherwise maneuvered into a variety of lithium ion battery configurations depending on design specifications and spatial constraints.
The high content of the heat-resistant particles amassed between the confronting inner face surfaces of the electrodes provides the separator with robust thermal stability well above 130° C. The heat-resistant particles will not soften, melt, swell, or chemically react with the liquid electrolyte solution even at the extreme ends of the conceivable operating temperature window of the lithium ion battery; rather, they remain compressed in place between the confronting inner face surfaces of the negative and positive electrodes. Nor will the heat-resistant particles sacrifice lithium ion conductivity at normal or elevated temperatures. The lithium ions can migrate around the heat-resistant particles and through the porous inert polymer material without much resistance. This is because the very small size of dissolved lithium ions in the liquid electrolyte solution can easily traverse the pore openings contained in the porous inert polymer material.
The fact that the porous inert polymer material may soften or melt at elevated temperatures (i.e., above 100° C.) does not significantly impact the structure or functionality of the separator. As mentioned before, the separator is compressed between the negative electrode and the positive electrode by an applied compressive force to promote intimate contact between the separator and each electrode at their respective contacting interfaces. The applied compressive force is also sufficient to prevent collapse or fragmentation of the heat-resistant particles that mostly constitute the separator should the porous inert polymer material that binds the many particles together soften or melt. The compressive and frictional forces acting on the heat-resistant particles are generally strong enough to withstand the effects of volumetric, structural, and/or phase changes that may occur in the porous inert polymer material. In fact, upon softening or melting, the porous inert polymer material would likely stay confined to a localized spatial volume defined by surrounding heat-resistant particles and then re-solidify when the temperature falls to a sufficient extent.
The separator can be fabricated by a phase-separation process in which the porous inert polymer material is precipitated out of a polymer solution that has been imbibed into the interstices of a layer of the heat-resistant particles. The free-standing separator produced by this process is handleable and can be assembled into an electrochemical battery cell between the negative and positive electrodes by conventional techniques without falling apart. The separator is situated between the negative and positive electrodes under an applied compressive force so that the heat-resistant particles extend between the confronting inner face surfaces of the electrodes to provide a porous and non-electrically conductive physical barrier. The porous inert polymer material contained in the separator allows the separator to be handled and situated between the electrodes during assembly of the electrochemical battery cell.
The phase-separation separator fabrication process involves forming a layer of the heat-resistant particles to a thickness consistent with the desired thickness of the separator such as, for example, between about 20 μm and about 50 μm. To form this layer, a liquid dispersion of the heat-resistant particles may be applied to a surface at a generally uniform thickness by any suitable technique followed by removal of the liquid. The layer of the heat-resistant particles is then soaked with the polymer solution. The polymer solution includes a relatively small amount of an inert polymer material, for example, between about 0.1 and 15 wt. %, dissolved in a miscible solvent mixture conducive to polymer phase separation. The miscible solvent mixture contains a polymer solvent and a polymer non-solvent with a higher boiling point than the polymer solvent. An appropriate volumetric ratio of the polymer solvent to the polymer non-solvent in the miscible solvent mixture ranges from about 5:1 to about 120:1.
The layer of the heat-resistant particles imbibed with the polymer solution is then heated to precipitate the porous inert polymer material through phase-separation. The applied heat does not affect the heat-resistant particles but does selectively evaporate the polymer solvent first followed by the polymer non-solvent. Evaporation of the polymer solvent causes the dissolved inert polymer material to precipitate out of the polymer solution. The precipitated inert polymer material and the polymer non-solvent remain significantly intermingled but phase separated at this point. The subsequent evaporation of the polymer non-solvent leaves behind empty pore openings to form the porous inert polymer material. When the miscible solvent mixture is completely evaporated, the porous inert polymer material, which has a porosity of about 20% to 80%, is formed and settles coextensively throughout the interstices naturally contained in the layer of the heat-resistant particles. The binding strength of the porous inert polymer material is sufficient to hold the heat-resistant particles together into a thin, handleable, and unified layer.
BRIEF DESCRIPTION OF THE DRAWINGS
<div id="p-0018" num="0017" class="description
TECHNICAL FIELD
The technical field of this disclosure relates generally to separators for a secondary lithium ion battery and, more specifically, to a separator formed predominantly of heat-resistant particles. The many heat-resistant particles are held together as a thin-layered, handleable, and unified mass by a porous inert polymer material. In an electrochemical battery cell of a lithium ion battery, the separator is situated between confronting inner face surfaces of a positive electrode and a negative electrode under an applied compressive force. Methods for making this type of separator by phase-separation are also disclosed.
BACKGROUND
Secondary (i.e., rechargeable) lithium ion batteries have been implemented as a power source into a wide variety of stationary and portable applications. Their structure and electrochemical reaction mechanism provide them with several desirable characteristics including a relatively high energy density, a relatively low internal resistance, a general non-appearance of any memory effect when compared to other types of rechargeable batteries, for example, nickel-cadmium batteries, and a low self-discharge rate. These characteristics have made lithium ion batteries the preferred mobile power source for portable consumer electronics such as laptop computers and cell phones. Larger-scale versions that interact with a multitude of interconnected systems have also been designed and manufactured by the automotive industry in an effort to improve vehicle fuel efficiency and reduce atmospheric pollution. The powertrains of hybrid electric vehicles (HEV) and extended range electric vehicles (EREV), for example, rely on the cooperative effort of lithium ion batteries and a hydrocarbon-fueled internal combustion engine to generate torque for vehicle propulsion.
A lithium ion battery generally contains one or more individual electrochemical battery cells that include a negative electrode, a positive electrode, and a porous polymeric separator sandwiched between the confronting inner face surfaces of the electrodes under a compressive force. The negative electrode generally includes a lithium host material that stores intercalated lithium at a relatively low electrochemical potential (relative to a lithium metal reference electrode). The positive electrode generally includes a lithium-based active material that stores intercalated lithium at a higher electrochemical potential than the lithium host material (relative to the same lithium metal reference electrode). The interadjacent porous separator includes opposed major surfaces that intimately contact the confronting inner face surfaces of the electrodes, and has typically been composed of a polyolefin such as polyethylene and/or polypropylene. A main function of the separator is to provide a porous and electrically insulative mechanical support barrier between the negative and positive electrodes. Each of the negative electrode, the positive electrode, and the separator is wetted with a liquid electrolyte solution that can communicate lithium ions. The liquid electrolyte solution is typically a lithium salt dissolved in a non-aqueous liquid solvent.
An interruptible external circuit electrically connects the negative electrode and the positive electrode to provide an electrical current path around the separator to electrochemically balance the migration of lithium ions. Metallic current collectors intimately associated with each electrode supply and distribute electrons to and from the external circuit depending on the operating state of the electrochemical battery cell. The external circuit can be coupled to an electrical load (during discharge) or an applied voltage from an external power source (during charging) through conventional electronic connectors and related circuitry. A voltage of approximately 2.5V to 4.3V is usually attained in each electrochemical battery cell during battery discharge. Greater overall battery power levels can be achieved, if necessary, by linking together a suitable number of similar electrochemical battery cells with their negative and positive electrodes connected in series or in parallel to corresponding common terminals. Current lithium ion batteries intended to be used in a vehicle powertrain typically include anywhere from 10 to 150 individual electrochemical battery cells. Several of these lithium ion batteries can be further connected in series or in parallel and packaged together to form a lithium ion battery pack that achieves a desired overall voltage and current capacity.
The individual electrochemical battery cell of a lithium ion battery operates by reversibly transporting lithium ions between the negative electrode and the positive electrode. The liquid electrolyte solution facilitates transport of the lithium ions through the separator. The flow direction of the lithium ions depends on whether the electrochemical batter cell is operating in a discharge state or a charge state. The lithium ions migrate from the negative electrode to the positive electrode during discharge and vice-versa during charging. The flow direction of the electrons through the external circuit mimics that of the lithium ions.
The discharge phase of the electrochemical battery cell can proceed when the negative electrode contains a sufficiently high concentration of intercalated lithium while the positive electrode is sufficiently depleted. The interruptible external circuit, when closed, provokes extraction of the intercalated lithium from the negative electrode. The extracted lithium splits into lithium ions and electrons. The lithium ions dissolve into the liquid electrolyte solution and migrate through the separator towards the positive electrode where they intercalate into the lithium-based active material. The electrons flow through the external circuit from the negative electrode to the positive electrode (with the help of the metallic current collectors) to balance these half-reactions. The flow of electrons through the external circuit can be harnessed and fed through the external load until the concentration of intercalated lithium in the negative electrode falls below a minimum effective level or the external circuit is opened.
The charge phase of the electrochemical battery cell can proceed after a partial or full reduction of its available capacity (through the discharge phase). To charge or re-power the cell, the external circuit is subjected to an applied voltage that originates from an external power source and which is sufficient in magnitude to accomplish charging in a reasonable time frame. The applied voltage drives the reverse of the discharge phase electrochemical half reactions; that is, during charging, intercalated lithium is extracted from the positive electrode to produce lithium ions and electrons. The lithium ions are carried back to the negative electrode through the separator and the electrons are driven back to the negative electrode through the external circuit. The lithium ions and the electrons reunite and replenish the negative electrode with intercalated lithium for the next battery discharge phase. Many thousands of substantially full-power discharge/charge cycles can be accomplished over the practical lifetime of the electrochemical battery cell.
The lifetime and performance of the electrochemical battery cell can be adversely impacted by a wide variety of expected and unforeseen factors. Exposure of the electrochemical battery cell to temperatures of 100° C. and above can cause the polyolefin separator to shrink, soften, and even melt if the temperature approaches 130° C. Such high temperatures can be attributed to charging-phase heat generation, ambient atmospheric temperature, or some other source. The temperature-initiated physical distortion of the polyolefin separator may ultimately permit direct electrical contact between the negative and positive electrodes and cause the electrochemical cell to short-circuit. Battery thermal runaway is also a possibility if the electrodes come into direct electrical contact with one another to an appreciable extent. A separator that can function reliably at the high-temperatures possibly encountered in an electrochemical battery cell of a lithium ion battery without affecting lithium ion movement is therefore needed.
SUMMARY OF THE DISCLOSURE
A separator for use in a lithium ion battery that retains its functionality at high operating temperatures includes a collection of heat-resistant particles held together in a thin, handleable layer by a relatively small amount of a porous inert polymer material. The heat-resistant particles range in size from about 0.01 μm to about 10 μm and are randomly stacked and arranged to a thickness of about 20 μm to about 50 μm with the outermost, surface exposed heat-resistant particles delineating opposed major face surfaces of the separator. The many heat-resistant particles naturally form a coextensive network of interconnected interstices that extends through the separator between the opposed major face surfaces. The porous inert polymer material pervades these naturally-formed interstices to bond and hold the heat-resistant particles together as a unified, handleable mass yet still permit infiltration of an appropriate liquid electrolyte solution.
The heat-resistant particles are thermally stable at temperatures below 250° C. They may be ceramic particles, cross-linked thermoset polymer particles, and/or engineering thermoplastic polymer particles. Some examples of suitable ceramic particles include alumina, titania, silica, ceria, zirconia, silicon carbide, boron carbide, titanium nitride, silicon nitride, titanium silicide, tungsten silicide, aluminum boride, titanium boride, mullite, spodumene, zirconium silicate, sillimanite, and petalite. Some examples of suitable cross-linked thermoset polymer particles include those of polyimides, polyurethanes, phenol-formaldehyde resins, melamine formaldehyde resins, and epoxy resins. Some examples of suitable engineering thermoplastic polymer particles include those of a polyimide, polyethylene terephthalate, polyphenylene sulfide, polyetherketone, polyether ether ketone, polyphenylsulfone, and a polysulfone. The porous inert polymer material that holds together the heat-resistant particles may be any polymer material suitable for use in the operating environment of a lithium ion battery. Some examples of the porous inert polymer material include polyetherimide (PEI), polyvinylidene fluoride (PVdF), polyacrylonitrile (PAN), poly(methyl methacrylate) (PMMA), polyoxymethylene (POM), or mixtures thereof. The porosity or void volume of the porous inert polymer material is preferably about 20% to about 80%.
The separator is intended to be used in the assembly of an electrochemical battery cell for a lithium ion battery. The separator may be situated between a negative electrode and a positive electrode and be infiltrated with an appropriate liquid electrolyte solution. The heat-resistant particles present on the major face surfaces of the separator contact confronting inner face surfaces of the negative and positive electrodes under an applied compressive force. The separator electrically insulates and physically separates the electrodes to prevent a short-circuit while remaining permeable to the internal passage of lithium ions (and related anions) through the liquid electrolyte solution. When assembled, the entire thickness of the electrochemical cell (positive electrode, negative electrode, and separator) is usually between about 80 μm and about 350 μm. A plurality of these electrochemical cells, often numbering from 10 to 150, can be connected in series or in parallel with many other electrochemical cells to form a lithium ion battery which, in turn, can be connected in series or in parallel with several other lithium ion batteries to form a lithium ion battery pack. The relatively thin and flexible nature of the electrochemical cells allows them to be rolled, folded, bent, or otherwise maneuvered into a variety of lithium ion battery configurations depending on design specifications and spatial constraints.
The high content of the heat-resistant particles amassed between the confronting inner face surfaces of the electrodes provides the separator with robust thermal stability well above 130° C. The heat-resistant particles will not soften, melt, swell, or chemically react with the liquid electrolyte solution even at the extreme ends of the conceivable operating temperature window of the lithium ion battery; rather, they remain compressed in place between the confronting inner face surfaces of the negative and positive electrodes. Nor will the heat-resistant particles sacrifice lithium ion conductivity at normal or elevated temperatures. The lithium ions can migrate around the heat-resistant particles and through the porous inert polymer material without much resistance. This is because the very small size of dissolved lithium ions in the liquid electrolyte solution can easily traverse the pore openings contained in the porous inert polymer material.
The fact that the porous inert polymer material may soften or melt at elevated temperatures (i.e., above 100° C.) does not significantly impact the structure or functionality of the separator. As mentioned before, the separator is compressed between the negative electrode and the positive electrode by an applied compressive force to promote intimate contact between the separator and each electrode at their respective contacting interfaces. The applied compressive force is also sufficient to prevent collapse or fragmentation of the heat-resistant particles that mostly constitute the separator should the porous inert polymer material that binds the many particles together soften or melt. The compressive and frictional forces acting on the heat-resistant particles are generally strong enough to withstand the effects of volumetric, structural, and/or phase changes that may occur in the porous inert polymer material. In fact, upon softening or melting, the porous inert polymer material would likely stay confined to a localized spatial volume defined by surrounding heat-resistant particles and then re-solidify when the temperature falls to a sufficient extent.
The separator can be fabricated by a phase-separation process in which the porous inert polymer material is precipitated out of a polymer solution that has been imbibed into the interstices of a layer of the heat-resistant particles. The free-standing separator produced by this process is handleable and can be assembled into an electrochemical battery cell between the negative and positive electrodes by conventional techniques without falling apart. The separator is situated between the negative and positive electrodes under an applied compressive force so that the heat-resistant particles extend between the confronting inner face surfaces of the electrodes to provide a porous and non-electrically conductive physical barrier. The porous inert polymer material contained in the separator allows the separator to be handled and situated between the electrodes during assembly of the electrochemical battery cell.
The phase-separation separator fabrication process involves forming a layer of the heat-resistant particles to a thickness consistent with the desired thickness of the separator such as, for example, between about 20 μm and about 50 μm. To form this layer, a liquid dispersion of the heat-resistant particles may be applied to a surface at a generally uniform thickness by any suitable technique followed by removal of the liquid. The layer of the heat-resistant particles is then soaked with the polymer solution. The polymer solution includes a relatively small amount of an inert polymer material, for example, between about 0.1 and 15 wt. %, dissolved in a miscible solvent mixture conducive to polymer phase separation. The miscible solvent mixture contains a polymer solvent and a polymer non-solvent with a higher boiling point than the polymer solvent. An appropriate volumetric ratio of the polymer solvent to the polymer non-solvent in the miscible solvent mixture ranges from about 5:1 to about 120:1.
The layer of the heat-resistant particles imbibed with the polymer solution is then heated to precipitate the porous inert polymer material through phase-separation. The applied heat does not affect the heat-resistant particles but does selectively evaporate the polymer solvent first followed by the polymer non-solvent. Evaporation of the polymer solvent causes the dissolved inert polymer material to precipitate out of the polymer solution. The precipitated inert polymer material and the polymer non-solvent remain significantly intermingled but phase separated at this point. The subsequent evaporation of the polymer non-solvent leaves behind empty pore openings to form the porous inert polymer material. When the miscible solvent mixture is completely evaporated, the porous inert polymer material, which has a porosity of about 20% to 80%, is formed and settles coextensively throughout the interstices naturally contained in the layer of the heat-resistant particles. The binding strength of the porous inert polymer material is sufficient to hold the heat-resistant particles together into a thin, handleable, and unified layer.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a generalized perspective illustration of a lithium ion battery that includes several adjacent electrochemical battery cells, each of which includes a negative electrode, a positive electrode, and a separator sandwiched between the two electrodes.
FIG. 2 is an enlarged, exploded cross-sectional view of one of the electrochemical battery cells shown in FIG. 1 along with its associated metallic current collectors. The components of the electrochemical battery cell and the metallic current collectors are idealized representations that are not necessarily drawn to scale.
FIG. 3 is a graph that compares the thermal stability of a specific and exemplary separator comprised predominantly of heat resistant-particles and a conventional monolayer polypropylene separator.
FIG. 4 is a graph that compares the cycle performance of a specific and exemplary separator comprised predominantly of heat resistant-particles and a conventional monolayer polypropylene separator.
DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS
An exemplary and generalized illustration of a lithium ion battery 10 is depicted in FIG. 1 . The lithium ion battery 10 shown here includes several rectangularly-shaped electrochemical battery cells 12 that are each bracketed by metallic current collectors. The electrochemical battery cells 12 are stacked side-by-side in a modular configuration and connected in series (although a parallel connection is also permitted). The lithium ion battery 10 can be connected serially or in parallel to other similarly constructed lithium ion batteries to form a lithium ion battery pack that exhibits the voltage and current capacity demanded for a particular application. It should be understood the lithium ion battery 10 shown here is only a schematic illustration. FIG. 1 is meant to show the relative position and physical interactions of the various components that constitute the electrochemical battery cells 12 (i.e., the electrodes and the separator); it is not intended to inform the relative sizes of the electrochemical battery cells' components, to define the number of electrochemical battery cells 12 in the lithium ion battery 10 , or to limit the wide variety of structural configurations the lithium ion battery 10 may assume. Various structural modifications to the lithium ion battery 10 shown in FIG. 1 are possible despite what is explicitly illustrated.
The electrochemical battery cell 12 contained in the lithium ion battery 10 includes a negative electrode 14 , a positive electrode 16 , and a separator 18 situated between the two electrodes
14 , 16 . Each of the negative electrode 14 , the positive electrode 16 , and the separator 18 is wetted with a liquid electrolyte solution that is able to communicate lithium ions. A negative-side metallic current collector 20 that includes a negative polarity tab 22 is located between the negative electrodes 14 of adjacent electrochemical cells 12 . Likewise, a positive-side metallic current collector 24 that includes a positive polarity tab 26 is located between neighboring positive electrodes 16 . The negative polarity tab 22 is electrically coupled to a negative terminal 28 and the positive polarity tab 26 is electrically coupled to a positive terminal 30 . The electrochemical battery cell 12 and the metallic current collectors
20 , 24 are pressed together by a compressive force F normally applied by the battery's housing or an internal structural component such as an end plate or divider. This applied compressive force F presses the metallic current collectors
20 , 24 , against the electrodes
14 , 16 and the electrodes
14 , 16 against the separator 18 to achieve intimate interfacial contact between the adjacent components.
An exploded cross-sectional view of the electrochemical battery cell 12 and its associated metallic current collectors
20 , 24 is generally illustrated in FIG. 2 . The negative electrode 14 includes an inner face surface 32 and an outer face surface 34 relative to the location of the separator 18 . The positive electrode 16 similarly includes an inner face surface 36 and an outer face surface 38 . The inner face surface 32 of the negative electrode 14 may, but is not required to, encompass a larger two-dimensional surface area than the inner face surface 36 of the positive electrode 16 , as shown. When assembled into the electrochemical battery cell 12 , the inner face surfaces 32 , 36 of the negative and positive electrodes
14 , 16 confront one another and are pressed against a negative-side major face surface 40 and a positive-side major face surface 42 of the separator 18 , respectively, under the applied compressive force F. Such pressed-engagement occurs generally uniformly along the entire interface of the major face surfaces 40 , 42 of the separator 18 and the corresponding portions of the inner face surfaces 32 , 36 of the electrodes
14 , 16 . The negative-side metallic current collector 20 is formed against the outer face surface 34 of the negative electrode 14 and the positive-side metallic current collector 24 is formed against the outer face surface 38 of the positive electrode 16 . Both of the metallic current collectors
20 , 24 engage their respective electrode outer face surfaces 34 , 38 over an appreciable interfacial surface area to facilitate the efficient collection and distribution of free electrons.
The electrochemical cell 12 is generally thin and flexible. A typical thickness of the electrochemical cell 12 extending from the outer face surface 34 of the negative electrode 12 to the outer face surface 38 of the positive electrode 16 is about 80 μm to about 350 μm. Each electrode
14 , 16 is preferably about 30 μm to 150 μm thick and the separator 18 is preferably about 20 μm to 50 μm thick. The metallic current collectors
20 , 24 are normally about 5 μm to 20 μm thick. The relatively thin and flexible nature of the electrochemical battery cell 12 and its associated metallic current collectors
20 , 24 allows them to be rolled, folded, bent, or otherwise maneuvered into a variety of lithium ion battery configurations depending on design specifications and spatial constraints. The lithium ion battery 10 may, for example, include a number of distinct electrochemical battery cells 12 that have been fabricated, cut, aligned, and layed-up next to one another or, in an alternative embodiment, the cells 12 may be derived from a continuous layer that is folded back-and-forth over itself many times.
The negative electrode 14 includes a lithium host material that stores intercalated lithium at a relatively low electrochemical potential (relative to a lithium metal reference electrode) such as, for example, graphite or lithium titanate. The lithium host material may be intermingled with a polymeric binder material to provide the negative electrode 14 with structural integrity. The lithium host material is preferably graphite and the polymeric binder material is preferably one or more of polyvinyldiene fluoride (PVdF), an ethylene propylene diene monomer (EPDM) rubber, or a carboxymethoxy cellulose (CMC). Graphite is normally used to make the negative electrode 14 because, on top of being relatively inert, its layered structure exhibits favorable lithium intercalation and deintercalation characteristics which help provide the electrochemical battery cell 12 with a suitable energy density. Commercial forms of graphite that may be used to construct the negative electrode 14 are available from Timcal Graphite and Carbon (headquartered in Bodio, Switzerland), Lonza Group (headquartered in Basel, Switzerland), and Superior Graphite (headquartered in Chicago, Ill.). The negative-side metallic current collector 20 associated with the negative electrode 14 is preferably a thin-film copper foil that coextensively contacts the outer face surface 34 of the negative electrode 14 .
The positive electrode 16 includes a lithium-based active material that stores intercalated lithium at a higher electrochemical potential than the lithium host material used to make the negative electrode 14 (also relative to a lithium metal reference electrode). The same polymeric binder materials that may be used to construct the negative electrode 14 (PVdF, EPDM, CMC) may also be intermingled with the lithium-based active material to provide the positive electrode 16 with structural integrity. The lithium-based active material is preferably a layered lithium transition metal oxide, such as lithium cobalt oxide (LiCoO 2 ), a spinel lithium transition metal oxide, such as spinel lithium manganese oxide (LiMn X O Y ), a lithium polyanion, such as a nickel-manganese-cobalt oxide [Li(Ni X Mn Y CO z )O 2 ], lithium iron phosphate (LiFePO 4 ), or lithium fluorophosphate (Li 2 FePO 4 F), or a mixture of any of these materials. Some other suitable lithium-based active materials that may be employed as all or part of the lithium-based active material include lithium nickel oxide (LiNiO 2 ), lithium aluminum manganese oxide (Li X Al Y Mn 1-Y O 2 ) and lithium vanadium oxide (LiV 2 O 5 ), to name but a few alternatives. The positive-side metallic current collector 24 associated with the positive electrode 16 is preferably a thin-film aluminum foil that coextensively contacts the outer face surface 38 of the positive electrode 16 .
The separator 18 , as shown best in FIG. 2 , is comprised predominantly of heat- resistant particles 44 held together by a small amount of a porous inert polymer material 46 . The heat- resistant particles 44 have a diameter that ranges from about 0.01 μm to about 10 μm. They are randomly stacked to a thickness T of the separator 18 that preferably ranges from about 25 μm to about 50 μm. Such stacking naturally forms a coextensive network of interconnected interstices around the particles 46 and through the separator 18 from one side to the other. The outermost, surface-exposed heat resistant particles 44 delineate the major face surfaces 40 , 42 of the separator 18 . The interstices formed between the heat- resistant particles 44 are occupied by the porous inert polymer material 46 . In terms of the composition of the separator 18 , the heat- resistant particles 44 are present at about 75 wt. % to about 95 wt. % and, preferably, about 85 wt. % to about 95 wt. %, while the porous inert polymer material 46 is present at about 5 wt. % to about 25 wt. % and, preferably, about 5 wt. % to about 15 wt. %.
The separator 18 functions as a thin and electrically insulative mechanical barrier layer that physically separates the confronting inner face surfaces 32 , 36 of the electrodes
14 , 16 to prevent a short-circuit in the electrochemical battery cell 12 . The separator 18 is also sufficiently porous to permit infiltration of the liquid electrolyte solution and the internal passage of dissolved lithium ions. Compression of the separator 18 within the electrochemical battery cell 12 presses the heat- resistant particles 44 exposed along the major face surfaces 40 , 42 of the separator 18 against the corresponding inner face surfaces 32 , 36 of the electrodes
14 , 16 . The intervening heat- resistant particles 44 located between the major face surfaces 40 , 42 are closely situated so they can shift and interact with each other to structurally support the thickness T of the separator 18 should the porous inert polymer material 46 begin to lose its binding capability on account of elevated temperatures.
The heat- resistant particles 44 contained in the separator 18 are thermally stable at temperatures below 250° C. The high content of the heat- resistant particles 44 amassed between the confronting inner face surfaces 32 , 36 of the electrodes
14 , 16 provides the separator 18 with robust thermal and chemical stability well above 130° C. A wide variety of materials may constitute the heat- resistant particles 44 such as ceramic particles, cross-linked thermoset polymer particles, engineering thermoplastic polymer particles, or a mixture of one or more of these types of particles. Some examples of suitable ceramic particles include alumina, titania, silica, ceria, zirconia, silicon carbide, boron carbide, titanium nitride, silicon nitride, titanium silicide, tungsten silicide, aluminum boride, titanium boride, mullite, spodumene, zirconium silicate, sillimanite, petalite, and mixtures thereof. Some examples of suitable cross-linked thermoset polymer particles include those of polyimides, polyurethanes, phenol-formaldehyde resins, melamine formaldehyde resins, epoxy resins, and mixtures thereof. Some examples of suitable engineering thermoplastic polymer particles include those of a polyimide, polyethylene terephthalate, polyphenylene sulfide, polyetherketone, polyether ether ketone, polyphenylsulfone, a polysulfone, and mixtures thereof.
The porous inert polymer material 46 that holds together the heat- resistant particles 44 may be any polymer material suitable for use in the operating environment of the electrochemical battery cell 12 . The void volume of the pores defined in the porous inert polymer material 46 is preferably in the range of about 20% to about 80%. The very small size of the dissolved lithium ions contained in the liquid electrolyte solution can easily migrate around the heat- resistant particles 44 and through such pores without much resistance. The porous inert polymer material 46 contained in the separator 18 , although typically present at all times, is not necessarily needed to sustain separation of the confronting inner face surfaces 32 , 36 of the electrodes
14 , 16 once the electrochemical battery cell 12 is assembled; rather, it is more instrumental in allowing the separator 18 to be handled and situated between the electrodes
14 , 16 during assembly of the electrochemical battery cell 12 . A few specific examples of the porous inert polymer material 46 include polyetherimide (PEI), polyvinylidene fluoride (PVdF), polyacrylonitrile (PAN), poly(methyl methacrylate) (PMMA), polyoxymethylene (POM), and mixtures thereof.
A rise in temperature that breaches 130° C. in the electrochemical cell 12 can be endured by the separator 18 without a sacrifice in functionality. The heat- resistant particles 44 will not soften, melt, swell, or chemically react with the liquid electrolyte solution even at the extreme ends of the conceivable operating temperature window of the lithium ion battery 10 ; rather, as a consequence of the applied compressive force F, they simply remain compressed in place between the inner face surfaces 32 , 36 of the <figure-callout id="16" label="electrodes" filenames="US09287540-20160315-D00000.png,US09
CLAIMS
Claims ( 16 )
The invention claimed is:
1. A secondary lithium ion battery that comprises a plurality of electrochemical battery cells connected in series or in parallel, at least one of the electrochemical battery cells comprising:
a negative electrode that includes an inner face surface;
a positive electrode that includes an inner face surface that confronts the inner face surface of the negative electrode; and
a separator situated between the negative electrode and the positive electrode that includes a negative-side major face surface and a positive-side major face surface, the negative side major face surface and the positive-side major face surface being pressed against the inner face surface of the negative electrode and the inner face surface of the positive electrode, respectively, under an applied compressive force, the separator comprising:
an amount of heat-resistant particles that have diameters ranging from about 0.01 μm to about 10 μm, the heat-resistant particles being stacked to a thickness of the separator, which ranges from about 20 μm to about 50 μm, so as to delineate and extend all the way through the separator between the negative-side major face surface and the positive-side major face surface of the separator, the stacking of the heat-resistant particles defining interstices between the particles and causing heat-resistant particles at the negative-side and positive-side major face surfaces to experience pressed contact with the inner face surfaces of the negative and positive electrodes, the amount of the heat-resistant particles present in the separator ranging from about 75 wt. % to about 95 wt. %; and
an amount of a porous inert polymer material that occupies the interstices formed between the heat-resistant particles the amount of the porous inert polymer material present in the separator ranging from about 25 wt. % to about 5 wt. %.
2. The lithium ion battery of claim 1 , further comprising:
a negative-side current collector that is formed against an outer face surface of the negative electrode, the outer face surface of the negative electrode facing opposite the inner face surface of the negative electrode;
a positive-side current collector that is formed against an outer face surface of the positive electrode, the outer face surface of the positive electrode facing opposite the inner face surface of the positive electrode; and
a liquid electrolyte solution that is infiltrated into the separator and wets both the negative and positive electrodes, the liquid electrolyte solution being able to communicate lithium ions between the negative and positive electrodes and through the separator.
3. The lithium ion battery of claim 1 , wherein the negative electrode includes a lithium host material and the positive electrode includes a lithium-based active material, wherein each of the lithium host material and the lithium-based active material stores intercalated lithium, and wherein the lithium-based active material stores intercalated lithium at a higher electrochemical potential, relative to a lithium metal reference electrode, than the lithium host material.
4. The lithium ion battery of claim 1 , wherein the heat-resistant particles comprise ceramic particles, cross-linked thermoset polymer particles, engineering thermoplastic polymer particles, or a mixture thereof.
5. The lithium ion battery of claim 4 , wherein the heat-resistant particles comprise particles of at least one of alumina, titania, silica, ceria, zirconia, silicon carbide, boron carbide, titanium nitride, silicon nitride, titanium silicide, tungsten silicide, aluminum boride, titanium boride, mullite, spodumene, zirconium silicate, sillimanite, petalite, a polyimide, a polyurethane, a phenol-formaldehyde resin, a melamine formaldehyde resin, an epoxy resin, polyethylene terephthalate, polyphenylene sulfide, polyetherketone, polyether ether ketone, polyphenylsulfone, polysulfone, or a mixture thereof.
6. The lithium ion battery of claim 1 , wherein the porous inert polymer material contains pores that provide the porous inert polymer material with a void volume of about 20% to about 80%.
7. The lithium ion battery of claim 1 , wherein the porous inert polymer material comprises polyetherimide, polyvinylidene fluoride, polyacrylonitrile, poly(methyl methacrylate), polyoxymethylene, or a mixture thereof.
8. The lithium ion battery set forth in claim 4 , wherein the heat-resistant particles comprise at least one of alumina, titania, silica, ceria, zirconia, silicon carbide, boron carbide, titanium nitride, silicon nitride, titanium silicide, tungsten silicide, aluminum boride, titanium boride, mullite, spodumene, zirconium silicate, sillimanite, petalite, or a mixture thereof.
9. The lithium ion battery set forth in claim 4 , wherein the heat-resistant particles comprise at least one of a polyimide, a polyurethane, a phenol-formaldehyde resin, a melamine formaldehyde resin, an epoxy resin, or a mixture thereof.
10. The lithium ion battery set forth in claim 4 , wherein the heat-resistant particles comprise at least one of a polyimide, polyethylene terephthalate, polyphenylene sulfide, polyetherketone, polyether ether ketone, polyphenylsulfone, polysulfone, or a mixture thereof.
11. The lithium ion battery set forth in claim 1 , wherein the amount of the heat-resistant particles present in the separator ranges from about 85 wt. % to about 95 wt. % and the amount of the porous inert polymer material present in the separator ranges from about 15 wt. % to about 5 wt. %.
12. A lithium ion battery that comprises a plurality of electrochemical battery cells, at least one of the electrochemical battery cells comprising:
a negative electrode that includes an inner face surface;
a positive electrode that includes an inner face surface that confronts the inner face surface of the negative electrode;
a separator situated between the negative electrode and the positive electrode and including a negative-side major face surface and a positive-side major face surface that define a thickness of the separator ranging from 20 μm to 50 μm, the negative-side major face surface and the positive-side major face surface being pressed against the inner face surface of the negative electrode and the inner face surface of the positive electrode, respectively, under an applied compressive force, the separator comprising heat-resistant particles that are stacked across the thickness of the separator so as to delineate the negative-side major face surface and the positive-side major face surface and to extend all the way between the negative-side major face surface and the positive-side major face surface, the heat-resistant particles having diameters ranging from 0.01 μm to 10 μm and the stacking of the heat-resistant particles defining interstices between the particles and causing heat-resistant particles at the negative-side and positive-side major face surfaces to experience pressed contact with the inner face surfaces of the negative and positive electrodes, the separator further comprising a porous inert polymer material that occupies the interstices formed between the heat-resistant particles, and wherein the separator includes 75 wt. % to 95 wt. % of the heat-resistant particles and 25 wt. % to 5 wt. % of the porous inert polymer material; and
a liquid electrolyte solution that is infiltrated into the separator and wets both the negative and positive electrodes, the liquid electrolyte solution being able to communicate lithium ions between the negative and positive electrodes and through the separator.
13. The lithium ion battery set forth in claim 12 , wherein the negative electrode includes a lithium host material and the positive electrode includes a lithium-based active material, wherein each of the lithium host material and the lithium-based active material stores intercalated lithium, and wherein the lithium-based active material stores intercalated lithium at a higher electrochemical potential, relative to a lithium metal reference electrode, than the lithium host material.
14. The lithium ion battery set forth in claim 12 , wherein the heat-resistant particles comprise at least one of alumina, titania, silica, ceria, zirconia, silicon carbide, boron carbide, titanium nitride, silicon nitride, titanium silicide, tungsten silicide, aluminum boride, titanium boride, mullite, spodumene, zirconium silicate, sillimanite, petalite, or a mixture thereof.
15. The lithium ion battery set forth in claim 12 , wherein the heat-resistant particles comprise at least one of a polyimide, a polyurethane, a phenol-formaldehyde resin, a melamine formaldehyde resin, an epoxy resin, or a mixture thereof.
16. The lithium ion battery set forth in claim 12 , wherein the heat-resistant particles comprise at least one of a polyimide, polyethylene terephthalate, polyphenylene sulfide, polyetherketone, polyether ether ketone, polyphenylsulfone, polysulfone, or a mixture thereof.
US13/149,117
2011-05-31
2011-05-31
Separators for a lithium ion battery
Active
2034-07-18
US9287540B2
( en )
Priority Applications (3)
Application Number
Priority Date
Filing Date
Title
US13/149,117
US9287540B2
( en )
2011-05-31
2011-05-31
Separators for a lithium ion battery
DE102012208726.5A
DE102012208726B4
( en )
2011-05-31
2012-05-24
Process for manufacturing a separator for a lithium-ion battery
CN201210175392.6A
CN102810656B
( en )
2011-05-31
2012-05-31
Lithium ion battery dividing plate
Applications Claiming Priority (1)
Application Number
Priority Date
Filing Date
Title
US13/149,117
US9287540B2
( en )
2011-05-31
2011-05-31
Separators for a lithium ion battery
Publications (2)
Publication Number
Publication Date
US20120308872A1
US20120308872A1 ( en )
2012-12-06
US9287540B2
true
US9287540B2 ( en )
2016-03-15
Family
ID=47173551
Family Applications (1)
Application Number
Title
Priority Date
Filing Date
US13/149,117
Active
2034-07-18
US9287540B2
( en )
2011-05-31
2011-05-31
Separators for a lithium ion battery
Country Status (3)
Country
Link
US
( 1 )
US9287540B2
( en )
CN
( 1 )
CN102810656B
( en )
DE
( 1 )
DE102012208726B4
( en )
Cited By (20)
* Cited by examiner, â Cited by third party
Publication number
Priority date
Publication date
Assignee
Title
US10008749B2
( en )
2016-06-19
2018-06-26
GM Global Technology Operations LLC
Lithium ion battery
US10050313B2
( en )
2016-06-19
2018-08-14
GM Global Technology Operations LLC
Lithium ion battery
US10056590B2
( en )
2016-08-31
2018-08-21
GM Global Technology Operations LLC
Methods of making separators for lithium ion batteries
US10312545B2
( en )
2008-08-05
2019-06-04
Sion Power Corporation
Application of force in electrochemical cells
US10418668B2
( en )
2017-07-07
2019-09-17
GM Global Technology Operations LLC
Electrolyte system including complexing agent to suppress or minimize metal contaminants and dendrite formation in lithium ion batteries
US10581119B2
( en )
2017-07-07
2020-03-03
GM Global Technology Operations LLC
Polymeric ion traps for suppressing or minimizing transition metal ions and dendrite formation or growth in lithium-ion batteries
US10581117B2
( en )
2017-07-07
2020-03-03
GM Global Technology Operations LLC
Iron ion trapping van der Waals gripper additives for electrolyte systems in lithium-ion batteries
US10629947B2
( en )
2008-08-05
2020-04-21
Sion Power Corporation
Electrochemical cell
US10680222B2
( en )
2017-12-19
2020-06-09
GM Global Technology Operations LLC
Method of making thermally-stable composite separators for lithium batteries
US10868306B2
( en )
2017-05-19
2020-12-15
Sion Power Corporation
Passivating agents for electrochemical cells
US10944094B2
( en )
2017-05-19
2021-03-09
Sion Power Corporation
Passivating agents for electrochemical cells
US11456459B2
( en )
2011-06-17
2022-09-27
Sion Power Corporation
Plating technique for electrode
US11588209B2
( en )
2018-08-21
2023-02-21
Applied Materials, Inc.
Ultra-thin ceramic coating on separator for batteries
US11791511B2
( en )
2019-11-19
2023-10-17
Sion Power Corporation
Thermally insulating compressible components for battery packs
US11824228B2
( en )
2019-11-19
2023-11-21
Sion Power Corporation
Compression systems for batteries
US11923495B2
( en )
2020-03-13
2024-03-05
Sion Power Corporation
Application of pressure to electrochemical devices including deformable solids, and related systems
US11978917B2
( en )
2019-11-19
2024-05-07
Sion Power Corporation
Batteries with components including carbon fiber, and associated systems and methods
US11984575B2
( en )
2019-11-19
2024-05-14
Sion Power Corporation
Battery alignment, and associated systems and methods
WO2024107405A1
( en )
2022-11-14
2024-05-23
Piersica, Inc.
Polymer composition and methods for making same
US12394817B2
( en )
2019-06-21
2025-08-19
Sion Power Corporation
Methods, systems, and devices for applying forces to electrochemical devices
Families Citing this family (53)
* Cited by examiner, â Cited by third party
Publication number
Priority date
Publication date
Assignee
Title
DE102010011414A1
( en )
*
2010-03-15
2011-09-15
Li-Tec Battery Gmbh
Lithium ion cell with intrinsic protection against thermal runaway
CN102299286B
( en )
*
2011-08-01
2014-09-03
å为ææ¯æéå ¬å¸
Battery diaphragm and preparation method and lithium ion battery thereof
WO2013071043A2
( en )
*
2011-11-10
2013-05-16
Dow Global Technologies Llc
Polymeric porous substrates including porous particles
CN104303346B
( en )
*
2012-03-27
2018-04-13
约翰éæ§å¶ææ¯å ¬å¸
Polysulfone coatings for high-voltage lithium-ion battery cells
JP2013222582A
( en )
2012-04-16
2013-10-28
Sony Corp
Secondary battery, battery pack, electric vehicle, power storage system, power tool, and electronic equipment
JP6290205B2
( en )
*
2012-07-20
2018-03-07
ãã¼ã¨ã¼ã¨ã¹ã¨ã ã½ã·ã¨ã¿ã¹ã»ã¨ã¼ããã¢ï¼¢ï½ï½ï½ ï¼³ï½
Electrochemical cell
CN104769742A
( en )
2012-07-30
2015-07-08
æ²ç¹åºç¡å ¨çææ¯æéå ¬å¸
High temperature melt integrity separator
US9502729B2
( en )
*
2012-08-29
2016-11-22
Corning Incorporated
Ion-conducting composite electrolyte comprising path-engineered particles
US9059451B2
( en )
2012-10-18
2015-06-16
GM Global Technology Operations LLC
Coatings for lithium titanate to suppress gas generation in lithium-ion batteries and methods for making and use thereof
WO2014093519A1
( en )
2012-12-13
2014-06-19
Applied Materials, Inc.
Ceramic coating on battery separators
US9034519B2
( en )
2013-01-18
2015-05-19
GM Global Technology Operations LLC
Ultrathin surface coating on negative electrodes to prevent transition metal deposition and methods for making and use thereof
US9412986B2
( en )
2013-07-31
2016-08-09
GM Global Technology Operations LLC
Porous composite structures for lithium-ion battery separators
US9331323B2
( en )
2013-08-21
2016-05-03
GM Global Technology Operations LLC
Cross-linked multilayer porous polymer membrane battery separators
US9865854B2
( en )
2013-09-30
2018-01-09
GM Global Technology Operations LLC
Lithium ion battery separators and electrodes
US9531004B2
( en )
2013-12-23
2016-12-27
GM Global Technology Operations LLC
Multifunctional hybrid coatings for electrodes made by atomic layer deposition techniques
US9564639B2
( en )
2014-02-12
2017-02-07
GM Global Technology Operations LLC
High performance silicon electrodes having improved interfacial adhesion between binder and silicon
CN103904276B
( en )
*
2014-03-28
2017-09-19
ä¸èæ°è½æºç§ææéå ¬å¸
Composite porous isolating membrane and electrochemical appliance
US10347934B2
( en )
2014-09-26
2019-07-09
Ut-Battelle, Llc
Shear activated impact resistant electrolyte
CN104377329B
( en )
*
2014-11-04
2017-01-11
ä¸å½ç§å¦é¢éå²çç©è½æºä¸è¿ç¨ç 究æ
Heat-resistant flame-retardant diaphragm and preparing method thereof
US10243188B2
( en )
2015-06-09
2019-03-26
GM Global Technology Operations LLC
Separator for lithium-based batteries
US10243241B2
( en )
2015-12-01
2019-03-26
GM Global Technology Operations LLC
Lithium ion battery with transition metal ion traps
US10396360B2
( en )
2016-05-20
2019-08-27
Gm Global Technology Operations Llc.
Polymerization process for forming polymeric ultrathin conformal coatings on electrode materials
US10164245B2
( en )
2016-09-19
2018-12-25
GM Global Technology Operations LLC
High performance silicon electrodes having improved interfacial adhesion between binder, silicon and conductive particles
CN110268563B
( en )
*
2017-02-24
2023-03-28
æ¥æ¬çç¿æ ªå¼ä¼ç¤¾
Binder composition for nonaqueous secondary battery, functional layer, slurry composition for functional layer, and nonaqueous secondary battery
US10741812B2
( en )
2017-06-19
2020-08-11
GM Global Technology Operations LLC
Acid-scavenging functional separators for power performance of lithium ion electrochemical cells
US11183714B2
( en )
*
2017-09-20
2021-11-23
GM Global Technology Operations LLC
Hybrid metal-organic framework separators for electrochemical cells
CN107732107A
( en )
*
2017-10-09
2018-02-23
å®å¾½éç¾æ°ææç§ææéå ¬å¸
A kind of preparation method of lithium ion battery ceramic diaphragm
US10347945B2
( en )
2017-12-08
2019-07-09
Ut-Battelle, Llc
Stabilized shear thickening electrolyte
US10777806B2
( en )
2018-03-29
2020-09-15
Baker Hughes, A Ge Company, Llc
Energy storage devices including at least one electrode comprising a metal diboride, and related methods
US10637100B2
( en )
2018-04-20
2020-04-28
Ut-Battelle, Llc
Fabrication of films and coatings used to activate shear thickening, impact resistant electrolytes
CN112602229B
( en )
2018-05-18
2023-08-01
éç¨æ±½è½¦ç¯çç§æè¿ä½æéè´£ä»»å ¬å¸
Hybrid lithium-ion capacitor battery with carbon-coated separator and method of making the same
US11393640B2
( en )
2018-06-20
2022-07-19
GM Global Technology Operations LLC
Water based hybrid lithium ion capacitor battery having a water-in-salt electrolyte
US10868307B2
( en )
2018-07-12
2020-12-15
GM Global Technology Operations LLC
High-performance electrodes employing semi-crystalline binders
US11228037B2
( en )
2018-07-12
2022-01-18
GM Global Technology Operations LLC
High-performance electrodes with a polymer network having electroactive materials chemically attached thereto
US11522225B2
( en )
*
2018-08-08
2022-12-06
Prologium Technology Co., Ltd.
Horizontal composite electricity supply element group
CN109309184A
( en )
*
2018-08-17
2019-02-05
ä½å±±å¸ä¸èªå çµç§æè¡ä»½æéå ¬å¸
A kind of preparation method of phenolic resin microspheres coating diaphragm
CN109849465A
( en )
*
2019-01-16
2019-06-07
ä¸èå¸æ¾³ä¸çµåæææéå ¬å¸
A kind of soft package lithium battery BOPP protective film
KR102827884B1
( en )
*
2019-12-13
2025-06-30
주ìíì¬ ìì§ìëì§ì루ì
Solid-liquid state hybrid electrolyte membrane, manufacturing method thereof and lithium secondary battery incluiding the same
DE112020006592T5
( en )
*
2020-01-23
2022-12-01
Rogers Corporation
Coated separator, electrochemical cell having a coated separator and method of making a coated separator
JP7791118B2
( en )
*
2020-06-19
2025-12-23
ã´ã¡ã«ã¿ ãã¤ã¯ãããããªã¼ ã²ã¼ã«ã·ã£ãã ããã ãã·ã¥ã¬ã³ã¯ãã« ãããã³ã°
Lithium-ion batteries with high specific energy density
CN112271272B
( en )
*
2020-08-31
2021-10-26
ä¸å大å¦
Three-dimensional porous lithium cathode protected by organic modification layer on surface and preparation method and application thereof
CN114597348B
( en )
2020-12-02
2024-06-11
éç¨æ±½è½¦ç¯çç§æè¿ä½æéè´£ä»»å ¬å¸
Method for manufacturing electrode by rolling
CN113193302B
( en )
*
2021-03-22
2023-03-03
æ·±å³ä¾çµå±æéå ¬å¸
Flame-retardant lithium-ion battery composite diaphragm and its preparation method and application
CN113437435B
( en )
*
2021-06-23
2023-05-26
æ±èææºæ°ææç§ææéå ¬å¸
Coating slurry, coating diaphragm and preparation method thereof
US11799083B2
( en )
2021-08-26
2023-10-24
GM Global Technology Operations LLC
Lithiation additive for a positive electrode
CN114512706B
( en )
*
2021-12-24
2023-08-04
åè¥å½è½©é«ç§å¨åè½æºæéå ¬å¸
Lithium ion battery diaphragm slurry and lithium ion battery diaphragm
DE102022117045A1
( en )
2022-07-08
2024-01-25
Bayerische Motoren Werke Aktiengesellschaft
Method and processing device for producing a storage cell for an electrical energy storage device, in particular a motor vehicle, and use of a processing device
US12609299B2
( en )
2022-08-03
2026-04-21
GM Global Technology Operations LLC
Protective particle coatings for electroactive material particles and methods of forming the same
CN115939667A
( en )
*
2022-11-23
2023-04-07
æ²³åéåæ°è½æºç§æè¡ä»½æéå ¬å¸
Lithium battery separator based on lithium titanium aluminum phosphate and mullite fiber and preparation method thereof
CN116247371B
( en )
*
2023-01-31
2025-10-31
å®å¾½å¾å£¹è½æºç§ææéå ¬å¸
High-temperature-resistant puncture-resistant coated diaphragm and preparation method thereof
WO2025128827A1
( en )
2023-12-14
2025-06-19
Safire Technology Group, Inc.
Systems and methods for enhancing safety of electrochemical cells via electrolyte thickening
CN118867575B
( en )
*
2024-09-19
2025-02-14
ä¸å½ç§å¦ææ¯å¤§å¦
Organic-inorganic hybrid battery diaphragm, preparation method thereof and water-based zinc ion battery
CN119208920B
( en )
*
2024-10-28
2026-04-14
åææ¥è½æ°è½æºåæ°ç§ææéå ¬å¸
Lithium supplementing diaphragm, preparation method thereof and lithium ion battery
Citations (5)
* Cited by examiner, â Cited by third party
Publication number
Priority date
Publication date
Assignee
Title
US5744264A
( en )
*
1996-06-13
1998-04-28
Valence Technology, Inc.
Lithium ion electrochemical cell
US20060008700A1
( en )
*
2004-07-07
2006-01-12
Yong Hyun H
Organic/inorganic composite porous film and electrochemical device prepared thereby
CN101222032A
( en )
2003-07-29
2008-07-16
æ¾ä¸çµå¨äº§ä¸æ ªå¼ä¼ç¤¾
Lithium-ion secondary battery
CN101714619A
( en )
2007-10-03
2010-05-26
ç´¢å°¼æ ªå¼ä¼ç¤¾
Diaphragm with heat-resistance insulating layer and non-water electrolyte secondary battery
CN102035043A
( en )
2009-09-25
2011-04-27
ä¸æµ·æ¯äºè¿ªæéå ¬å¸
Polymer porous membrane, preparation method thereof, polymer electrolyte, polymer battery and preparation method of battery
Family Cites Families (4)
* Cited by examiner, â Cited by third party
Publication number
Priority date
Publication date
Assignee
Title
US3749604A
( en )
1970-03-12
1973-07-31
Westinghouse Electric Corp
Heat resistant substrates and battery separators made therefrom
DE69637084T2
( en )
1995-08-28
2008-02-07
Asahi Kasei Emd Corporation
LITHIUM CELL AND METHOD FOR THE PRODUCTION THEREOF
US7604895B2
( en )
*
2004-03-29
2009-10-20
Lg Chem, Ltd.
Electrochemical cell with two types of separators
CN101913862B
( en )
*
2010-07-27
2012-07-25
大è¿æµ·äºå¤§å¦
Composite membrane for lithium ion battery and lithium ion battery using same
2011
2011-05-31
US
US13/149,117
patent/US9287540B2/en
active
Active
2012
2012-05-24
DE
DE102012208726.5A
patent/DE102012208726B4/en
active
Active
2012-05-31
CN
CN201210175392.6A
patent/CN102810656B/en
active
Active
Patent Citations (5)
* Cited by examiner, â Cited by third party
Publication number
Priority date
Publication date
Assignee
Title
US5744264A
( en )
*
1996-06-13
1998-04-28
Valence Technology, Inc.
Lithium ion electrochemical cell
CN101222032A
( en )
2003-07-29
2008-07-16
æ¾ä¸çµå¨äº§ä¸æ ªå¼ä¼ç¤¾
Lithium-ion secondary battery
US20060008700A1
( en )
*
2004-07-07
2006-01-12
Yong Hyun H
Organic/inorganic composite porous film and electrochemical device prepared thereby
CN101714619A
( en )
2007-10-03
2010-05-26
ç´¢å°¼æ ªå¼ä¼ç¤¾
Diaphragm with heat-resistance insulating layer and non-water electrolyte secondary battery
CN102035043A
( en )
2009-09-25
2011-04-27
ä¸æµ·æ¯äºè¿ªæéå ¬å¸
Polymer porous membrane, preparation method thereof, polymer electrolyte, polymer battery and preparation method of battery
Non-Patent Citations (5)
* Cited by examiner, â Cited by third party
Title
U.S. Appl. No. 12/974,094; Title: Battery Separators With Variable Porosity; filed Dec. 10, 2010; First Named Inventor: Hamid G. Kia.
U.S. Appl. No. 12/974,269; Title: Battery Separators With Variable Porosity; filed Dec. 10, 2010; First Named Inventor: Hamid G. Kia.
U.S. Appl. No. 13/045,563; Title: Integral Bi-Layer Separator-Electrode Construction for Lithium-Ion Batteries; filed Mar. 11, 2011 First Named Inventor: Xiaosong Huang.
U.S. Appl. No. 13/149,205; Title: Methods of Making Lithium Ion Battery Separators; filed May 31, 2011; First Named Inventor: Xiaosong Huang.
U.S. Appl. No. 13/217,455; Title: Lithium Ion Battery With Electrolyte-Embedded Separator Particles; filed 08/25/201; First Named Inventor: Ion C. Halalay.
Cited By (31)
* Cited by examiner, â Cited by third party
Publication number
Priority date
Publication date
Assignee
Title
US11735761B2
( en )
2008-08-05
2023-08-22
Sion Power Corporation
Application of force in electrochemical cells
US11121397B2
( en )
2008-08-05
2021-09-14
Sion Power Corporation
Application of force in electrochemical cells
US10312545B2
( en )
2008-08-05
2019-06-04
Sion Power Corporation
Application of force in electrochemical cells
US10320027B2
( en )
2008-08-05
2019-06-11
Sion Power Corporation
Application of force in electrochemical cells
US11108077B2
( en )
2008-08-05
2021-08-31
Sion Power Corporation
Application of force in electrochemical cells
US11108076B2
( en )
2008-08-05
2021-08-31
Sion Power Corporation
Application of force in electrochemical cells
US10629947B2
( en )
2008-08-05
2020-04-21
Sion Power Corporation
Electrochemical cell
US11456459B2
( en )
2011-06-17
2022-09-27
Sion Power Corporation
Plating technique for electrode
US10008749B2
( en )
2016-06-19
2018-06-26
GM Global Technology Operations LLC
Lithium ion battery
US10050313B2
( en )
2016-06-19
2018-08-14
GM Global Technology Operations LLC
Lithium ion battery
US10056590B2
( en )
2016-08-31
2018-08-21
GM Global Technology Operations LLC
Methods of making separators for lithium ion batteries
US11784297B2
( en )
2017-05-19
2023-10-10
Sion Power Corporation
Passivating agents for electrochemical cells
US10868306B2
( en )
2017-05-19
2020-12-15
Sion Power Corporation
Passivating agents for electrochemical cells
US10944094B2
( en )
2017-05-19
2021-03-09
Sion Power Corporation
Passivating agents for electrochemical cells
US12614711B2
( en )
2017-05-19
2026-04-28
Sion Power Corporation
Passivating agents for electrochemical cells
US10581117B2
( en )
2017-07-07
2020-03-03
GM Global Technology Operations LLC
Iron ion trapping van der Waals gripper additives for electrolyte systems in lithium-ion batteries
US10581119B2
( en )
2017-07-07
2020-03-03
GM Global Technology Operations LLC
Polymeric ion traps for suppressing or minimizing transition metal ions and dendrite formation or growth in lithium-ion batteries
US10418668B2
( en )
2017-07-07
2019-09-17
GM Global Technology Operations LLC
Electrolyte system including complexing agent to suppress or minimize metal contaminants and dendrite formation in lithium ion batteries
US10680222B2
( en )
2017-12-19
2020-06-09
GM Global Technology Operations LLC
Method of making thermally-stable composite separators for lithium batteries
US11588209B2
( en )
2018-08-21
2023-02-21
Applied Materials, Inc.
Ultra-thin ceramic coating on separator for batteries
US12394817B2
( en )
2019-06-21
2025-08-19
Sion Power Corporation
Methods, systems, and devices for applying forces to electrochemical devices
US11929523B2
( en )
2019-11-19
2024-03-12
Sion Power Corporation
Batteries, and associated systems and methods
US11978917B2
( en )
2019-11-19
2024-05-07
Sion Power Corporation
Batteries with components including carbon fiber, and associated systems and methods
US11984575B2
( en )
2019-11-19
2024-05-14
Sion Power Corporation
Battery alignment, and associated systems and methods
US12051829B2
( en )
2019-11-19
2024-07-30
Sion Power Corporation
Systems and methods for applying and maintaining compression pressure on electrochemical cells
US11824228B2
( en )
2019-11-19
2023-11-21
Sion Power Corporation
Compression systems for batteries
US11791511B2
( en )
2019-11-19
2023-10-17
Sion Power Corporation
Thermally insulating compressible components for battery packs
US11923495B2
( en )
2020-03-13
2024-03-05
S